Deco foil- surfaces HiGX - PVC or PET High gloss foil   Physical Properties    Sample : All-petg (0.25mm)     TEST ITEM UNIT RESULT TEST METHOD Tensile strength(T.D) N/§± 57.7 ISO 527-3 : 1995(*) Tensile strength(M.D) N/§¯ 68 ISO 527-3 : 1995(*) Elongation at break(T.D) % 432 ISO 527-3 : 1995(*) Elongation at break(M.D) % 402 ISO 527-3 : 1995(*)  * Specimen: Type 5, Speed of Testing: 50mm/min    NOTE      The test results on this test report are only limited to the samples and sample names provided by        the customer and JCT do not guarantee the quality of all products of the customer.      This test report shall not be used for public relation, advertisement, lawsuit and any other purposes        outside the scope of its defined usage.

DECO FOIL-furniture surfaces NEOREX - PVC deco foil   Physical Properties     Property Test Methed Membrane Pressing(0.3mm) Wrapping(0.20mm) Specific Gravity ASTM D_792 1.35 1.3 Tensile Strength(kg f/cn2) ASTM D_638 360(MD) 200(MD) Elongation(%) 120C*2min 200 300 Tear Strength(kg f/cn2) ASTM D 1004 80(MD) 80(TD) 80(MD) 80(TD) Dimemensional stability(%) 80C*30min 250*250mm 3(MD) 1(TD) 3(MD) 1(TD)   ASTM D 1526 70 70  Section I - Manufacturer Identification      Product Name: NEOREX & HiGX Deco foil (Rigid Thermofoil)      Manufactuere's Name: JCT Products      Address: 1941 Cheongsin-ro, Sinbuk-myeon, Pocheon-si, Gyeonggi-do, Korea      Telephone/Fax No.: +82-31-542-5786 / +82-31-542-5787    Section II - Hazarous Ingredients     Hazarous Componets CAS Number Vapor Pressure Weight % PVC Resin 9002-86-2 N/A 70 ~ 80% Plasticizer 68515-48-0 N/A 7 ~13% Impact Modifier 25053-09-1 N/A 9 ~ 13% Pigment Mixture N/A 4 ~ 5 % Stabilizer Mixture N/A 2 ~ 4 %  Section III - Physical/Chemical Charateristics      Boiling Point (F) : N/A      Vapor Density (Air = 1) : N/A      Solubility in Water : N/A      Appearance and Odor : N/A      Spefific Gravity (H©ü O = 1) : 1.2 ~ 1.4      Evaporation Rate : N/A    Section IV - Fire and Explosion Hazard Data      Flash Point : N/A      Flammable Limits in Air by Volume - Lower : N/A, Upper : N/A      Extinguishing Media CO©ü , Dry Chemical      Special Fire Fighting Procedures :        Use self containing breathing apparatus and full protective quipment        All Fires toxic gas      Unusual fire and explosion Hazards :        Decomposition Products include Hydrogen Chloride gas    Secton V - Health Hazard Data      Threshold Limit Value : N/A      Effects of Overexposure : N/A at usual Temperature      Emergency and First Aid Procedures :        Thess Products have no significant toxic hazard      Hazarous fumes are produced by combustion of high temperature decomposition      If exposed to fumes, flush affected area with water for 15 minutes and seek medical attention    Section VI - Reactivity Data      Stability : Stable      Condition to avoid : Avoid wet condition      Incompatibility (Materials to avoid) : Non reactive      Hazardous decomposition products : Hydrogen Chloride gas CO, CO©ü      Hazardous polymerization : Will not occur    Section VII - Spill or Leak Procedures      Step to be taken in case material is released or spilled : None      Waste disposal method : disposed in accordance with local regulations    Section VIII - Special Protection Information      Respiratory Protection (Spefify type) : None      Protective Gloves : None      Other protective equipment : None      Eye protection : None    Section IX - Special Precautions      Precautions to be taken in handling and storing : Store in cool dry area      Other precautions : Keep away from heat for prolonged preiods

DECO FOIL-furniture surfaces NEOREX ECO - PP deco foil   Physical Properties     No Standard Number Test Condition Method of the test Result Remarks 1   Bonding Test   Adhesive test Hot Water (80 degree) Remained 72 hours No remarkable changes Tested by JCT Products 2   Long duration climate test 60,70,80 degree 7 weeks   No test   3   Tropical Test 70degree, humidity 100% - 5weeks   No test   4   Ascending heat test 70degree-2 hours, 80/90/100degree - 1 hour   No test   5 DIN 68861-7 Dry heat test Temperature (70,100,140,180 degree) 16 hours Heat Resistance (80degree, Remained 16hours) for chaging surface test No remarkable changes Refer to 2014 test result 6 DIN 68861-8 Wet heat test Temperature (55,70,100µµ) 16Hours Heat Resistance (80degree, Remained 16hours) for chaging surface test No remarkable changes Refer to 2014 test result 7 DIN 68861-2 Abrasion test   Thermosetting resin:Wear Resistance(Taber, P-180-AA, weight-5.2N (500g) Abrasion loss : 0.11g/100 rotated ¸¶¸ð°ª : 383ȸ Refer to 2014 test result 8 DIN 68861-4 Scratching test   Thermosetting resin:Scratch(Hardness Test) 700g above Refer to 2014 test result 9 DIN 68861-1 Chemical Resistance test 16°¡Áö ¿À¿°¹°Áú(16~24½Ã°£ ¹æÄ¡) Spread 2% of Sodium hydroxide, Remained 6 hours, for chaging surface test No remarkable changes No remarkable changes Refer to 2010 test result 10 ISO 4892-2, DIN EN105 B O2 Light fastness test   Accelated weathering test of coating (QUV, 1000h) Chaging colour test No remarkable changes Refer to 2010 test result 11 ISO 354 Noise reduction coefficient(NRC)     No test   12 ISO 140 (part 3) Sound Transmission coefficient(STC)     No test    NOTE      The test results on this test report are only limited to the samples and sample names provided by        the customer and JCT do not guarantee the quality of all products of the customer.      This test report shall not be used for public relation, advertisement, lawsuit and any other purposes        outside the scope of its defined usage.

DECO FOIL-furniture surfaces FlexMetal - PET composite stainless looking foil   Physical Properties     Property Test Methed Value Tensile Strength 120mm(L)*10mm(W)*200mm/min L65 W60 Elongation 120mm(L)*10mm(W)*200mm/min L51 W45 Tear Strength 120mm(L)*10mm(W)*200mm/min L19 W17 Percentage of Contraction 100'c*10min Heating L0.04 W0.04 Adhesion 25mm*20mm*50mm/min(180'C/365'F) 1.2 Heat Resistance 180'C/356'5min Heating No peel Water Boiling Point Resistance 38'C/208'F*1hr Heating*1hr Leveling No peel Acid Resistance Deposit 5% CH3COOH * 72hr No change Alkail Resistance Deposit 5% NaOH * 72hr No change Surface Hardness Mistubishi Pencil Test(200g load) H Weatherabilaty W-O-M 100hr No change Ultraviolet Resistance QUV 24hr No change Erichsen Test After Cross Cutting Distance 5mm, Push 8mm No Peel Salt spray Resistance After Cross Cutting 5% NaCl * 240hr 1mm Creep  NOTE      The test results on this test report are only limited to the samples and sample names provided by        the customer and JCT do not guarantee the quality of all products of the customer.      This test report shall not be used for public relation, advertisement, lawsuit and any other purposes        outside the scope of its defined usage.

DECO FOIL-furniture surfaces Exterior foil - Acrylic composite foil   Physical Properties